Product Details:
|
| Material: | Hot Melt Granule | Color: | Transparent |
|---|---|---|---|
| Usage: | Aluminium Honeycomb Panel For Furniture And Exterior DecorationEx | Future: | Low Temperature And Environmentally-friendly |
| Manufacturing Method: | Cast Film | Aluminium Coil Thickness: | 0.5mm-0.7mm |
| Highlight: | 200 Mircons cast film,cast film 200 Mircons,Transparent cast film |
||
Grade:AH5020
Product:200Mircons Low Temperature Adhesive Cast Film For Aluminium Honeycomb Composite Panel
Decriptions
The polymer adhesive cast film for aluminum Honeycomb composite panels is based on the comprehensive research of domestic and overseas aluminum honeycomb adhesive, combined with the independent intellectual property rights. The polymer adhesive cast film is a thermoplastic adhesive material with no solvent, no formaldehyde, no benzene, no toluene and other harmful substances, 100% solid content. The polymer film is only sticky after being heated and melted, and then the adhesion between various substances is achieved under a certain pressure.Aluminium honeycomb panel is made up of multi-layer materials. Both the upper and lower layers are high-purity aluminum alloy sheets, the middle layer is aluminium honeycomb sheet.
AH5020 adhesive cast film is used for aluminium honeycomb composite panel with 100% of adhesive resins,which ensures the honeycomb panel bonding well and has excellent peel strength.The processing temperature is low,for which makes the honeycomb panel combination well at lower temperature in high production speed.
Application
AH5020 polymer adhesive film is used for Aluminium honeycomb Panel,which can be used for exterior decoration and aluminium furniture.The aluminium coil thickness range is form 0.5mm to 0.7mm.
Advantages
Excellent bonding strength and low processing temperature
Good anti-aging and long-lasting bonding performances
no solvent, no formaldehyde, no benzene, no toluene and other harmful substances,green and environmentally-friendly
A2 grade fire resistance.
Physical Properties
| Item | Unit | Testing Standard | 200 microns thickness | Remark |
| Density | g/cm3 | ASTM D1505 | 0.925 | |
| Tensile Strength | MPa | ASTM D638 | 8.7 | |
| Elongation at Break | % | ASTM D638 | >65 | |
| T-peel strength | 50N/mm | GB/T 2791 | >75 | 170℃ 2min |
| T-peel strength | 50N/mm | GB/T 2791 | >55 | 170℃ 40s |
| Width | Mm | GB/T 6673-1986 | ±5 | |
| Thickness | Mm | GB/T 6672-1986 | ±0.002 |
♦These are typical properties and not intended as specification
Specifications:
Width: 50mm-1600mm (Customization available)
Length: 500m/ roll or customization
Processing Suggestions :
Adhesive Layer Structure: AL+AH5020+aluminium honeycomb sheet +AH5020+AL
Bonding Temperature: 150℃-180℃
Metal Surface: Phosphating or chromizing treatment and pre-degreasing treatment can avoid dust pollutants.
QC Standard: IS09001:2015
Packing and Storage:
12 Rolls/Pallet,60- 80 KG/Roll (Customization available)；
Keep in a dry cool place. Avoid direct sunlight, ventilation, and moisture. The storage period at room temperature is 12 months. If the film color changes and elongation is found to decrease by 50%, do not use it.
.
Remarks: The above information and technical data are based on our existing product knowledge and experience. We do not guarantee the above content and do not assume legal responsibility. Customers must do a sample test before using our products to ensure the best processing conditions.